| Oscillation Frequency (Fosc) | 8.000 MHz | |
| Frequency Tolerance | Fosc0.1% ~ 0.3% (MAX) | Referenced to initial measurements: 0.3% |
| Resonator Impedance | 30 (MAX) | Referenced to initial measurements: 10 |
| Operating Temperature Range | -20 ~ +70 | |
| Temperature Stability | 0.5% (MAX) | (-40 ~ +85) |
| Insulation Resistance | 100M min | (D.C. 100V) |
| Aging (10 years) | 0.3% | |
| Storage Temperature Range | -40 ~ +85 | |
| Test Temperature & Humidity Condition | +10 ~ +30, 40% ~ 80% RH | Standard measurement condition: 202, 655% RH |
| Dimensions | 10.0 (MAX) x 6.0 (MAX) x 5.00.3 mm | Terminal pitch: 5.0 1.0 mm, Terminal diameter: 0.30.1 mm, Height: 4.0 (MAX) mm, Lead diameter: 0.50.1 mm |
| Lead Strength | Pulling: 0.5kg force for 10 sec. Bending: 0.25kg force, 90 bend | No mechanical damage, measured values meet Table 1. |
| Solderability | Immersed in resin for 5 sec, then in soldering bath (2355) for 50.5 sec. | Solder coverage 90% of terminal surface. |
| Storage in High Temp. | 85 for 100 hours, then 1 hour natural condition. | Measured value shall meet Table 1. |
| Storage in Low Temp. | -25 for 100 hours, then 1 hour natural condition. | Measured value shall meet Table 1. |
| Humidity | 402, 90~95% RH for 100 hours, then 1 hour natural condition. | Measured value shall meet Table 1. |
| Thermal Shock | -55 (30 min) to +85 (30 min) cycle, 5 times, then 1 hour natural condition. | Measured value shall meet Table 1. |
| Resistance to Soldering Heat | Immersed up to 2.0 mm from root in solder bath (2655) for 101 seconds, then 1 hour natural condition. | Measured value shall meet Table 1. |
| Random Drop | 3 times from 1m height onto concrete floor. | Measured value shall meet Table 1. |
| Vibration | 10 Hz to 55 Hz, 1.5mm amplitude, 3 axial directions, 1 hour/direction. | Measured value shall meet Table 1. |
| Composite Temperature/Humidity Cycle Test | 10 continuous cycles: 25 to -10 within 30 min (humidity uncontrolled below 25), then 24 hours at standard conditions. | Measured value shall meet Table 1. |